Hydrogen embrittlement (HE) and hydrogen-induced cracking (HIC) behaviour of a X65 steel pipeline weldment were investigated using slow strain rate tensile (SSRT) testing of specimens that were specifically extracted from different zones of the weldment (i.e., weld metal (WM), heat-affected zone (HAZ), and base metal (BM)). The WM was found to be the most susceptible zone to HE and HIC, while BM the least. Analysis of microstructure, fracture surface, secondary crack formation, and mechanical behaviour revealed that the high HE susceptibility of WM is correlated to microstructural features including Ti-rich inclusions, martensite/austenite (M/A) constituents, and prior austenite grain boundaries (PAGBs).
Get to know all about of Caltech Engineering Services product that is Bent beam sohic test. The products that are manufactured cater to the requirements of various industries like fertilizer, offshore upstream & downstream, cross country pipelines, onshore, marine contractors, engineering and construction.