The microstructure and high-temperature creep mechanisms of Ni-based Hastelloy C276 superalloy fabricated using wire and arc-based directed energy deposition were investigated systematically and innovatively. The microstructural investigation revealed that the as-fabricated samples comprise γ-Ni matrix and topologically close-packed (TCP) P phase precipitates. The γ matrix subgrains and grains are spread over multiple highly textured columnar dendrites, with a majority of γ <001> crystallographic orientations closely aligned along the deposition direction. Moreover, the interdendritic regions exhibit severe Mo segregation, P phase particles, and dislocation bands. Creep tests were conducted on miniature samples under various temperature and stress conditions, loaded either in the deposition direction (DD) or travel direction (TD). DD samples exhibit lower minimum strain rates, greater strains-to-failure, and longer creep rupture lifetimes than TD samples, indicating significan